溶胶-凝胶法在玻璃表面负载二氧化钛薄膜研究
关键词 溶胶-凝胶法 TiO2薄膜 光催化活性
毕业论文设计说明书（论文）外文摘要
Title The Study of Coating TiO2 Thin Film on Glass
Surface by Sol-gel Method
Abstract
The TiO2 sol were prepared through the hydrolysis of butyl titanate and water(1:3,molar ratio) with hydrochloric acid as catalyst and ethanol as solvent by sol-gel method. The TiO2 sol was coated on glass through the dipping - pulling method, and the TiO2 powders as well as TiO2 thin films were achieved by calcined the TiO2 sol and TiO2 coated glass respectively under 300℃, 450℃, and 600℃ for 2.5 h.The particle size, polymorphs and thermal stability were measured by N2 adsorption- desorption curve, X - ray diffraction(XRD) and TG analysis. Bisphenol A(BPA) was selected as model pollutant to explore the photocatalytic activity of TiO2 films. The results showed that the particle size of TiO2 powders ranged from 8 nm to 30 nm under different calcination temperatures. The amount of anatase phase in TiO2 powders increased at first then decreased with the increase of temperature. The anatase phase could not be observed at 600℃. With the increasing calcination temperature, the photocatalytic activity of TiO2 thin film first increased then decreased. This research provided some theoretical and experimental basis for the preparation of TiO2 thin film and its practical use.
Key words Sol-gel method TiO2 thin film photocatalytic activity
目 次
1 绪论 1
1.1 TiO2光催化作用 1
1.1.1 TiO2光催化机理 1
1.1.2 TiO2光催化影响因素 2
1.2 太阳能光催化集热管 3
1.2.1 概述 3
1.2.2 光催化集热管的工作原理 4
1.3 纳米TiO2的制备方法 5
1.3.1 固相法 5
1.3.2 气相法 6
1.3.3 液相法 7
1.4 纳米TiO2光催化薄膜的制备 8
1.4.1 电化学方法 8
1.4.2 化学气相沉积法 9
1.4.3 物理方法 9
1.4.4 液相沉积法 9
1.4.5 溶胶-凝胶法 10
1.5 溶胶-凝胶法制膜的影响因素 10
1.5.1 溶胶组成的影响 11
1.5.2 涂覆方式的影响 12
1.5.3 焙烧温度的影响 12
1.6 本论文的研究内容 12
2 实验材料和研究方法 13
2.1 实验材料及仪器 13
2.1.1实验材料及试剂 13
2.1.2 实验仪器及设备 13
2.2 TiO2的制备 14
2.2.1 TiO2溶胶的制备 14
下一篇：氟化石墨烯的水性分散液+文献综述